1. Scope

1.1 This test method describes procedures for microscopical determinations of the air content of hardened concrete and of the specific surface, void frequency, spacing factor, and paste-air ratio of the air-void system in hardened concrete (1) . Two procedures are described:

1.1.1 Procedure A,

the linear-traverse method (2, 3) .

1.1.2 Procedure B,

the modified point-count method (3, 4, 5, 6) .

1.2 This test method is based on prescribed procedures that are applied to sawed and lapped sections of specimens of concrete from the field or laboratory.

1.3 It is intended to outline the principles of this test method and to establish standards for its adequate performance but not to describe in detail all the possible variations that might be used to accomplish the objectives of this test method.

1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

1.5 This standard does not purport to address all of the safety concerns associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. For specific hazard statements see 8.3 and 10.1.

2. Referenced Documents (purchase separately) The documents listed below are referenced within the subject standard but are not provided as part of the standard.

ASTM Standards

C42/C42M Test Method for Obtaining and Testing Drilled Cores and Sawed Beams of Concrete

C125 Terminology Relating to Concrete and Concrete Aggregates

C138/C138M Test Method for Density (Unit Weight), Yield, and Air Content (Gravimetric) of Concrete

C173/C173M Test Method for Air Content of Freshly Mixed Concrete by the Volumetric Method

C231 Test Method for Air Content of Freshly Mixed Concrete by the Pressure Method

C666/C666M Test Method for Resistance of Concrete to Rapid Freezing and Thawing

C670 Practice for Preparing Precision and Bias Statements for Test Methods for Construction Materials

C672/C672M Test Method for Scaling Resistance of Concrete Surfaces Exposed to Deicing Chemicals

C823 Practice for Examination and Sampling of Hardened Concrete in Constructions

C856 Practice for Petrographic Examination of Hardened Concrete

D92 Test Method for Flash and Fire Points by Cleveland Open Cup Tester

American Concrete Institute Standards

Keywords

air content; air void parameters of hardened concrete; area-prepared surface required; average chord-length of voids; determination of air-void parameters; entrained void; entrapped void; grits for lapping hardened concrete; index point; lapping; length of traverse required; linear-traverse method; microscopical; number of points required; paste-air ratio; paste-air ratio modification; paste content; point-count method (modified); sample preparation for microscopical analysis; spacing factor; specific surface; void frequency; water void ;