BS EN 61788-18:2013 Superconductivity - Mechanical properties measurement. Room temperature tensile test of Ag- and/or Ag alloy-sheathed Bi-2223 and Bi-2212 composite superconductors, 2014
- EN61788-18{2013}e.pdf [Go to Page]
- Foreword
- Endorsement notice
- Annex ZA (normative) Normative references to international publications with their corresponding European publications
- 30290631-VOR.pdf [Go to Page]
- English [Go to Page]
- CONTENTS
- FOREWORD
- INTRODUCTION
- 1 Scope
- 2 Normative references
- 3 Terms and definitions
- 4 Principle
- 5 Apparatus [Go to Page]
- 5.1 General
- 5.2 Testing machine
- 5.3 Extensometer
- 6 Specimen preparation [Go to Page]
- 6.1 General
- 6.2 Length of specimen
- 6.3 Removing insulation
- 6.4 Determination of cross-sectional area (S0)
- 7 Testing conditions [Go to Page]
- 7.1 Specimen gripping
- 7.2 Setting of extensometer
- 7.3 Testing speed
- 7.4 Test
- 8 Calculation of results [Go to Page]
- 8.1 Modulus of elasticity (E)
- 8.2 0,2 % proof strength (Rp 0,2)
- 8.3 Tensile stress at specified strains (RA)
- 8.4 Fracture strength (Rf)
- 9 Uncertainty of measurement
- 10 Test report [Go to Page]
- 10.1 Specimen
- 10.2 Results
- 10.3 Test conditions
- Annex A (informative) Additional information relating to Clauses 1 to 14
- Annex B (informative) Uncertainty considerations
- Annex C (informative) Specific examples related to evaluation of uncertainties for Ag/Bi-2223 and Ag/Bi-2212 wires
- Bibliography
- Figures [Go to Page]
- Figure 1 – Typical stress-strain curve and definition of modulus of elasticity and 0,2 % proof strengths of an Ag/Bi-2223 wire externally laminated by brass foil
- Figure 2 – Typical stress-strain curve of an Ag/Bi-2223 wire where the 0,2 % proof strengths could not be determined and definition of tensile stresses at specified strains
- Figure A.1 – Low mass Siam twin type extensometer with a gauge length of ~ 12,3 mm (total mass ~ 0,5 g)
- Figure A.2 – Low mass double extensometer with a gauge length of ~ 25,6 mm (total mass ~ 3 g)
- Figure A.3 – An example of the extensometer provided with balance weight and vertical specimen axis
- Figure A.4 – Original raw data of an Ag/Bi-2223 wire measurement in form of load and displacement graph
- Figure A.5 – Typical stress versus strain of an Ag/Bi-2223 wire up to the elastic limit corresponding to the transition region from elastic to plastic deformation (point G)
- Figure C.1 – Measured stress versus strain curve for Bi-2223 wire
- Tables [Go to Page]
- Table A.1 – Results of relative standard uncertainty values achieved on different Ag/Bi-2223 wires during the international round robin tests
- Table A.2 – Selected data for F test for E0 of Sample E bare wire
- Table A.3 – Results of F-test for the variations of E0 of four kinds of Bi-2223 wires
- Table B.1 – Output signals from two nominally identical extensometers
- Table B.2 – Mean values of two output signals
- Table B.3 – Experimental standard deviations of two output signals
- Table B.4 – Standard uncertainties of two output signals
- Table B.5 – Coefficient of variations of two output signals
- Table C.1. – Load cell specifications according to manufacturer’s data sheet
- Table C.2 – Uncertainties from various factors for stress measurement
- Table C.3 – Uncertainties with respect to measurement of strain measurement
- Table C.4 – Summary of evaluated uncertainties caused by various factors
- Table C.5 – Results of uncertainty evaluation for the modulus of elasticity (E0 = 86,1 GPa) as a function of initial cross head rate
- Table C.6 – Uncertainties from various factors for stress measurement
- Table C.7 – Results of uncertainty evaluation for the stress (R = 42,5 MPa) as a function of initial strain rate
- Français [Go to Page]
- SOMMAIRE
- AVANT-PROPOS
- INTRODUCTION
- 1 Domaine d'application
- 2 Références normatives
- 3 Termes et définitions
- 4 Principe
- 5 Appareillage [Go to Page]
- 5.1 Généralités
- 5.2 Machine d'essai
- 5.3 Extensomètre
- 6 Préparation de l'éprouvette [Go to Page]
- 6.1 Généralités
- 6.2 Longueur de l'éprouvette
- 6.3 Retrait de l'isolation
- 6.4 Détermination de la surface de section (S0)
- 7 Conditions d'essai [Go to Page]
- 7.1 Serrage de l'éprouvette
- 7.2 Mise en place de l'extensomètre
- 7.3 Vitesse d'essai
- 7.4 Essai
- 8 Calcul des résultats [Go to Page]
- 8.1 Module d'élasticité (E)
- 8.2 Charge d'épreuve à 0,2 % (Rp 0,2)
- 8.3 Contrainte de traction pour des déformations spécifiées (RA)
- 8.4 Résistance à la rupture (Rf)
- 9 Incertitude de mesure
- 10 Rapport d'essai [Go to Page]
- 10.1 Eprouvette
- 10.2 Résultats
- 10.3 Conditions d’essai
- Annexe A (informative) Informations complémentaires relatives aux Articles 1 à 14
- Annexe B (informative) Considérations relatives à l'incertitude
- Annexe C (informative) Exemples spécifiques concernant l'évaluation des incertitudes pour les fils d'Ag/Bi-2223 et d'Ag/Bi-2212
- Bibliographie
- Figures [Go to Page]
- Figure 1 – Courbe contrainte-déformation type et définition du module d'élasticité et des charges d'épreuve à 0,2 % d'un fil d'Ag/Bi-2223 recouvert extérieurement d'une feuille de laiton
- Figure 2 – Courbe contrainte-déformation type d'un fil d'Ag/Bi-2223 lorsqu'il n'a pas été possible de déterminer les charges d'épreuve à 0,2 % et définition des contraintes de traction pour des déformations spécifiées
- Figure A.1 – Extensomètre de type jumeau de Siam avec une longueur entre repères d'environ 12,3 mm (masse totale d'environ 0,5 g)
- Figure A.2 – Extensomètre double à faible masse avec une longueur entre repères d'environ 25,6 mm (masse totale d'environ 3 g)
- Figure A.3 – Exemple d'extensomètre muni d'une masse d'équilibrage et d'un axe d'éprouvette vertical
- Figure A.4 – Données brutes originales d'une mesure de fil d'Ag/Bi-2223 se présentant sous la forme d'une courbe de charge et de déplacement
- Figure A.5 – Contrainte type en fonction de la déformation d'un fil d'Ag/Bi-2223 jusqu'à la limite élastique correspondant à la région de transitionentre déformation élastique et plastique (point G)
- Figure C.1 – Courbe de contrainte mesurée en fonctionde la déformation pour un fil de Bi-2223
- Tableaux [Go to Page]
- Tableau A.1 – Résultats des valeurs d'incertitude type relative obtenus sur différents fils d'Ag/Bi-2223 lors des essais interlaboratoires internationaux
- Tableau A.2 – Données sélectionnées pour l'essai F pour E0 de l'échantillon E de fil nu
- Tableau A.3 – Résultats de l'essai F pour les variations de E0de quatre types de fils de Bi-2223
- Tableau B.1 – Signaux de sortie de deux extensomètres nominalement identiques
- Tableau B.2 – Valeurs moyennes de deux signaux de sortie
- Tableau B.3 – Écarts types expérimentaux de deux signaux de sortie
- Tableau B.4 – Incertitudes-types de deux signaux de sortie
- Tableau B.5 – Coefficient de variation de deux signaux de sortie
- Tableau C.1 – Caractéristiques du dynamomètre en fonction des fiches de caractéristiques du fabricant
- Tableau C.2 – Incertitudes de divers facteurs de mesure de contrainte
- Tableau C.3 – Incertitudes concernant la mesure de déformation
- Tableau C.4 – Résumé des incertitudes évaluées provoquées par divers facteurs.
- Tableau C.5 – Résultats de l'évaluation d'incertitude pour le module d'élasticité (E0=86,1 GPa) en fonction de la vitesse de déplacement initiale
- Tableau C.6 – Incertitudes de divers facteurs de mesure de contrainte. .
- Tableau C.7 – Résultats d'évaluation d'incertitude pour la contrainte (R = 42,5 MPa) en fonction du taux de déformation initial [Go to Page]